聚酯防爆膜 VMPET
PET真空镀铝防爆膜(亦称太阳膜),实现玻璃防爆、防紫外线、隔热、隔视等功能。其清晰度高,色泽性能稳定均一;可使玻璃安全、美观、舒适;同时起到节能环保的作用。
产品物性表
Standard 参考标准 | Item No常用产品型号 | ||||||||
VPET- VLT5% | VPET-VLT10% | VPET-VLT18% | VPET-VLT30% | VPET-VLT45% | VPET-VLT70% | ||||
Item 物性项目 | Testing Methods 测试方法 | Unit 单位 | Typical Values标准值 | Typical Values标准值 | Typical Values标准值 | Typical Values标准值 | Typical Values标准值 | Typical Values标准值 | |
Thickness 厚度 | GB/T 6672-2001 | μm | 15-50 | 15-50 | 15-50 | 15-50 | 15-50 | 15-50 | |
拉伸 强度 Tensile Strength | MD | ASTM D882 | MPa | ≥170 | ≥170 | ≥170 | ≥170 | ≥170 | ≥170 |
TD | ≥170 | ≥170 | ≥170 | ≥170 | ≥170 | ≥170 | |||
断裂伸长率Elongation at Break | MD | ASTM D882 | % | ≤200 | ≤200 | ≤200 | ≤200 | ≤200 | ≤200 |
TD | ≤200 | ≤200 | ≤200 | ≤200 | ≤200 | ≤200 | |||
热收 缩率Heat Shrinkage | MD | ASTM D1204 | % | ≤3.0 | ≤3.0 | ≤3.0 | ≤3.0 | ≤3.0 | ≤3.0 |
TD | ≤3.0 | ≤3.0 | ≤3.0 | ≤3.0 | ≤3.0 | ≤3.0 | |||
湿润 张力Surface Tension | 镀层面Al side | GB/T 14216-2008 | mN/m | ≥48 | ≥48 | ≥48 | ≥48 | ≥48 | ≥48 |
非镀层面Non-Al side | ≥52 | ≥52 | ≥52 | ≥52 | ≥52 | ≥52 | |||
透光率ight Transmittance | 林尚SL162 | % | 5% | 10% | 18% | 30% | 45% | 70% | |
铝层厚度Al Thickness | - | ? | 280 | 200 | 180 | 160 | 110 | 40 | |
基膜雾度Base Film Haze | ASTM D-1003 | % | ≤2.0 | ≤2.0 | ≤2.0 | ≤2.0 | ≤2.0 | ≤2.0 | |
镀层均匀度Al Uniformity | ASTM D-1003 | % | 2 | 2 | 3 | 3 | 3 | 3 | |
镀层附着力Al Adhesion | QB/T 2358-1998 | N/15mm | 2.5 | 2.5 | 3 | 3 | 3 | 3 | |
常用厚度Common Thickness | 16μm、19μm、23μm、36μm、50μm |
重要提示
1.以上数据信息为本司测试所得,供客户试样或使用本品时参考;
2.产品的最终性能跟复合工艺有关系,使用不当会对产品造成破坏性损伤;
3.客户其他特殊要求最好与我司技术部门做详细沟通,以便产品更能适合客户使用。
1.具有玻璃防爆、防紫外线、隔热、隔视等功能。
广泛用于汽车窗膜、建筑窗膜、浴室夹层玻璃、室内外隔视玻璃等方面,